Nano Ribbon

Magnetic characteristics1.High saturation magnetic induction intensity(Bs)2.High frequency and low loss(Ps)

Specification:RNC/G
Manufacturer:Yongfeng Nanocrystalline Products Branch
Contact Person:Mr. Sun Origin:Haidian District,Beijing
Email:nano@atmcn.comTel:+86-010-58712641
More

 一、Introducing of Antainano®

1.1 Summary:

AT&M has the Nanocrystalline metallic materials with Hitachi Metals patent license, in 2006 obtained the ISO9001 quality system certification, in 2014 through the TS16949 system certification of automotive products, the production of high precision Antainano® nanocrystalline ribbon is more than 3000 tons.The precursor of Antainano® is amorphous ribbon (non-crystalline)obtained by rapid quenching at one million ℃/second from the molten metal consisting of Fe、Si、B、Cu、Nb,with after annealing treatment obtained the ultra fine size grain (~10nm). 

The notable feature of this new type of metallic functional materials1.jpg is that the short production process , one step forming, saving energy consumption. Its outstanding advantage is that both the Fe based amorphous alloy with high saturation magnetization (Bs) and cobalt based amorphous alloy with high permeability and low loss, can well satisfy the performance requirements of high frequency  low loss. Ribbons mainly use in the production of high precision inductors, high frequency switching power supply with magnetic core, high frequency transformer and high-end magnetic amplifier and other high-end products. Related core devices are mainly used in digital electronic products, smart electricity meter,  inverter of the photovoltaic generation and new energy vehicle charging, driving system, to meet the requirements of power electronics technology to the development of high frequency, high current, small, energy saving and other requirements. 


1.2 Material Characteristic of Antainano®:

1.png

1.3 Advantage of Antainano®:

3.png


1.4 Development Direction of Soft Magnetic Material:

4.png

※ Energy saving and miniaturization

Nanocrystalline alloy can replace cobalt based amorphous alloy, amorphous permalloy and ferrite, with high frequency power electronic components and electronic information field to small, lightweight, efficient development trend.。


二、Major Application of Antainano®

22.png

2.1 Common Mode Choke:

23.png—High saturate induction—reduce volume of transformers

—Excellent impedance frequency characteristic

—Outstanding ability to resist balance current

—Excellent thermal stability 

24.png


2.2 Small Transformer:

25.png—High saturate induction—reduce volume of transformers

—High permeability and low coercivity—improve efficiency, lower exciting power and reduce copper loss

—Low core loss—reduce temperature rise of transformers

—Excellent thermal stability—with the serving temperature of -55℃~130℃ for long time

 

27.png26.png




 


2.3 Large Power Transformer Cores –Cutting:

28.png—Low core loss

—High operation flux density

—High operation temperature




30.png
29.png


 

 

 

 

 

 

 

 

 

 



2.4 Current Transformer:

31.png—High permeability,low coercivity

—Low core loss,low phase error,low amplitude

—Higher saturation magnetic flux density and wider measuring current range  

—Low permenbility ,high anti drift ability. Sensitive to small leakage current and good ability of resisting large current impact  

—Excellent temperature stability


类别Trademark

Thickness

(mm)

Stacking Factor

B800T,≥

B800T,≥

Coercive force

Hc A/m

SFN18S**-600.018±0.002

0.78±0.01

0.80±0.01

0.82±0.01

0.84±0.01

0.86±0.01

0.88±0.01

1.11.5
FN18S**-30
FN22S**-600.022±0.002
FN22S**-30
FN26S**-600.026±0.002
FN26S**-30
FN30S**-600.030±0.002
FN30S**-30
BFN14B**-600.014±0.002
FN18B**-600.018±0.002
FN18B**-30
FN22B**-600.022±0.002
FN22B**-30
FN26B**-600.026±0.002
FN26B**-30
FN30B**-600.030±0.002
FN30B**-30

B

N

FN´´N10-**

0.014±0.002

0.018±0.002

0.022±0.002

2.5
FN´´N05-**
FN´´N02-**
FN´´N01-**
NFN´´N01-**0.026±0.002